A novel green diluent for the preparation of poly(4-methyl-1-pentene) membranes via a thermally-induced phase separation method

Abstract

The use of green solvents satisfies safer chemical engineering practices and environmental security. Herein, myristic acid (MA)—a green diluent—was selected to prepare poly-(4-methyl-1-pentene) (PMP) membranes with bicontinuous porous structure via a thermally induced phase separation (TIPS) process to maintain a high gas permeability. Firstly, based on the Hansen solubility parameter ‘distance’, Ra, the effect of four natural fatty acids on the PMP membrane structure was compared and studied to determine the optimal green diluent, MA. The thermodynamic phase diagram of the PMP-MA system was calculated and presented to show that a liquid-liquid phase separation region could be found during the TIPS process and the monotectic point was around 34.89 wt%. Then, the effect of the PMP concentration on the morphologies and crystallization behavior was systematically investigated to determine a proper PMP concentration for the membrane preparation. Finally, PMP hollow fiber (HF) membranes were fabricated with a PMP concentration of 30 wt% for the membrane performance characterization. The resultant PMP HF membranes possessed good performances that the porosity was 70%, the tensile strength was 96 cN, and the nitrogen flux was 8.20 ± 0.10 mL·(bar·cm2·min)−1 . We believe that this work can be a beneficial reference for people interested in the preparation of PMP membranes for medical applications.